To carry out microgravity material science experiments effectively on the ground

Go to the profile of Xinghong Luo
Oct 14, 2019
0
0

Compared with the expensive space microgravity experiment with rare opportunity and long period, the ground drop tube solidification experiment has many advantages, such as low cost, stable microgravity level, short period, easy to get and good reproducibility.

However, due to the short microgravity time, usually only a few seconds, when the conventional containerless droplet method is used, only some refractory alloys can finish solidification, while alloys with relative low melting point may still be in the process of supercooling and have not started solidification until falling to the bottom of drop tube.

Even for those alloys that can finish solidification, due to the overlap of effects of supercooling and microgravity, it is difficult to pick out the microgravity effect on solidification. That’s one of the main reasons why not too many studies have been carried out using drop tube although it has many advantages.

In view of this, we put forward a new method of drop tube experiment, i.e., rod sample half-melting method. As shown in the following figure, at top of drop tube, electromagnetic induction heating method is adopted to melt only the upper half part of the rod-shaped sample, so that the lower half part of the sample remains in the state of unmelted solid. When the heating power is turned off and the sample is dropped, the lower half part of the sample can act as a cold end and seed crystal to make the upper half part of the sample solidify immediately. In this method, taking full advantage of the microgravity time, for example, 3.2 seconds provided by a 50-meter-high drop tube, the sample may grow a few millimeters to a dozen millimeters. Meanwhile, sample solidified in normal gravity environment with the same experimental parameters can also be obtained by this method. By comparing the solidified samples in microgravity and gravity environment, we can know exactly the influence of microgravity environment on the solidification of alloys, so as to make the ground-based microgravity solidification experiment using drop tube more efficient, which can be used as an effective supplement to space microgravity material experiment and a means of preliminary research.

By using this new method, we have studied the microgravity effect in the solidification of single crystal superalloys, eutectic alloys, and composites etc, and obtained very good results. Recently, we studied the microstructure of TC8 titanium alloy solidified under microgravity and normal gravity. It was found that the average solidification velocity was faster than the buoyancy convection velocity and solute diffusion velocity in melt. In this case, we used to tend to think that the effect of gravity on solidification can be negligible. However, the microstructure observation result indicated that the microstructure solidified under microgravity and normal gravity were significantly different. There must be some factor induced by gravity at work. After further analysis, we drew a conclusion that it was the hydrostatic pressure caused by gravity that affected the solidification behavior of the alloy by affecting the heat dissipation of the melt. This result shows that the effect of hydrostatic pressure should not be ignored when analyzing the influence of gravity on the solidification structure of materials.

The complete article about this work can be found in the journal of npj Microgravity.

Link: https://rdcu.be/bT1vV

Go to the profile of Xinghong Luo

Xinghong Luo

Prof., Institute of Metal Research, Chinese Academy of Sciences

Microgravity material science and technology reaseach

No comments yet.